INCONEL Alloy X (HX) (UNS N06002)


Ni Bal, Cr 21.8, Fe 18.5, Mo 9.0, Mn 1.00, C 0.1, Si 1.00,S 0.03, Co 1.5, W 0.6

 

High Performance Alloys stocks and produces INCONEL Alloy X in this grade in the following forms: Bar, sheet, plate, disk, machined, forged. Request quote on this grade.

 

Overview

Download Bulletin 4 pgs - Or view as HTML

 

Heat Resistant (UNS N06002)
INCONEL Alloy X is a wrought nickel base alloy with excellent high temperature strength and oxidation resistance. All of the product forms are excellent in terms of forming and welding. Although INCONEL Alloy X is primarily noted for heat and oxidation resistance it also has good resistance to chloride stress-corrosion cracking and has good resistance to carburization, excellent resistance to reducing or carburizing atmospheres. Alloy X is one of the most widely used nickel base superalloys for gas turbine engine components.

AMS 5754 has no yield or tensile strength requirements, but it does require a hardness maximum and stress rupture minimums. Strong and Oxidation Resistant to 2200 Deg. F (1200 Deg. C) - INCONEL Alloy X is a solid solution strengthened grade has good strength and oxidation resistance up to 2200 Deg. F (1200 Deg. C).


Characteristics

RESISTANCE TO OXIDATION
The outstanding oxidation resistance of INCONEL Alloy X is illustrated below. Tests were conducted by exposing samples to dry air at 2000 Deg. F. and to dry air pressurized to 300 psi at 1750 Deg. F. Two criteria for evaluating oxidation resistance are weight change and depth of corrosion penetration. INCONEL Alloy X excels in both respects due to the formation of a protective, tenacious oxide film.

RESISTANCE TO CARBURIZATION AND NITRIDING
INCONEL Alloy X also resists carburization and nitriding, two common conditions which often lead to early failure in high-temperature alloys. After 100 hours in petroleum coke, four other materials were completely penetrated by carburization; whereas, Alloy X specimens showed no carburization at all. Of ten materials evaluated in an atmosphere of hydrogen, nitrogen and ammonia at 1100 Deg. F. and 25,00 psi for 64 days, Alloy X had a nitride case less than one-fourth as thick as the closest competitive material without intergranular attack.

 

Applications

INCONEL Alloy X finds use in petrochemical process equipment and gas turbines in the hot combustor zone sections. Also used for structural components in industrial furnace applications because of the excellent oxidation resistance.

INCONEL Alloy X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operating for 8700 hours at 2150 Deg. F. Furnace trays, used to support heavy loads, have been exposed to temperatures up to 2300 Deg. F. in an oxidizing atmosphere without bending or warping. Alloy X is equally suitable for use in jet engine tailpipes, afterburner components, turbine blades, nozzle vanes, cabin heaters, and other aircraft parts.

Gas turbine combustion cans and ducting, heat-treating equipment.

Alloy X has wide use in gas turbine engines for combustion zone components such as transition duct, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Furnace rolls of this alloy were still in good condition after operating for 8,700 hours at 2150 degrees F (1177 degrees C). INCONEL Alloy X is also used in the chemical process industry for retorts, muffles, catalyst support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.

Useful Properties for Aircraft and Furnace Parts - INCONEL Alloy X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operation for 8,700 hours at 2150 Deg. F (1177 Deg. C).

 


Chemistry

Chemical Requirements

Ni

Cr

Mo

Mn

C

Si

Fe

Max

Bal

23.0

10.0

1.00

0.15

1.00

20.0

Min

20.5

8.00

0.05

17.0


Tensile Data

Mechanical Property Requirements

Ultimate Tensile

Yield Strength (0.2% OS)

Elong. in 2 in. or 50mm or 4D, min., %

R/A

Hardness

Min

95 KSi

35 KSi

35

Max

Min

655 MPa

240 MPa

Max


Specifications

Form

Standard

Metal Type

UNS N06002

Bar

ASTM B572 AMS 5754

Wire

AMS 5798W AMS 5798C

Sheet

ASTM B435 AMS 5536

Plate

ASTM B435 AMS 5536

Tube
AMS 5587 AMS 5588 ASTM B619 ASTM B622
Pipe
AMS 5587 AMS 5588 ASTM B619 ASTM B622

Fitting

ASTM B366

Forging

AMS 5754 GE B50TF31

Weld Wire

A5.14 ERNiCrMo-2

Weld Electrode
A5.11 ENiCrMo-2

Din

2.4665


 

Machining

Machinability RATING: 27% of B-1112

TYPICAL STOCK REMOVAL RATE: 45 surface feet/minute with high speed tools, 125 surface feet/minute with carbide.

COMMENTS:
Care must be taken to make sure there are rigid machine setup and sharp tools, so that work hardening and surface glazing do not occur. INCONEL Alloy X is machinable in both the wrought and cast form. Low cutting speeds and an ample flow of coolant are required.

Suggested tool angles for single point tungsten carbide tools are 8- to 10-Deg. side-rake angle from cutting edge, 5- to 8-Deg. back-rake angle, 5- to 7-Deg. end relief angle, and 15- to 30-Deg. side cutting-edge angle. Nose radius should be 1/32 to 1/16 inch.

High-speed steel drills should be ground to an included angle of 135 to 140 Deg. with a clearance angle of 10 degrees. The web should be thinned down to about one-third the web-thickness of a standard drill.

Better finishes can be obtained by increasing the speed and decreasing the feed. Automatic screw machines are not recommended because speeds are generally excessive and carbide-tipped tools will not hold up. A sulfur-base cutting fluid should be used for machining this alloy. All traces of cutting fluid should be removed prior to heat-treatment or high temperature service.

The following table may be used as a guide in machining INCONEL Alloy alloy X. The figures will be modified by such factors as tool size and type, type of machining equipment, size of stock, and nature of cut.

 

Machining Guide for INCONEL Alloy X

Operation

Tool
Type

Speed
SFPM

Feed
Inch Per Rev.

Depth in Cut
Inch

Cut Type

Turning

 

WC

68
88

.009-.016
.006-.009

.050-.100
.011-.015

Rough
Finish

HSS

18
21

.007-.011
.003-.008

.025-.045
.008-.011

Rough
Finish

Facing

 

WC

68
88

.009-.016
.006-.009

.040-.075
.011-.015

Rough
Finish

HSS

18
21

.007-.011
.003-.008

.025-.045
.008-.011

Rough
Finish

Boring

WC

42
53

.009-.016
.006-.009

.043-.060
.012-.015

Rough
Finish

Drilling

HSS

18
25

.003-.007
.002-.004

---
---

Rough
Finish

Reaming

HSS

25
35

.006-.010
---

---
.012-.015

Rough
Finish

Shaping

 

WC

20
30

---
.005-.010

.060-.090
.018-.025

Rough
Finish

HSS

13
15

---
.005-.010

.050-.080
.018-.025

Rough
Finish

Milling

HSS

15
25

1/2-1 IPM

.100-.200 in. cut

Rough
Finish

 

Heat-Treatment

All wrought forms of INCONEL Alloy X are furnished in the solution heat-treated condition unless otherwise specified. The standard heat-treatment is at a temperature of 2150 Deg. F (1177 Deg. C) followed by rapid cooling. Other heat-treatment temperatures also may be effective for certain forms and conditions.

The properties listed here are average values based on laboratory test conducted by the manufacturer. They are indicative only of the results obtained in such tests and should not be considered as guaranteed maximums or minimums. Materials must be tested under actual service conditions to determine their suitability for a particular purpose. All data represent the average of six or less tests unless otherwise noted. All data shown for material aged for 1,000, 4,000, 8,000, and/or 16,000 hours are based on tests of a single heat. The secondary units (metric) used in this booklet are those of the SI system.


 